    Rudis Material Praeparatio & Ratio
Seged NDFEB magnetica proprietatibus
Gradus REMANENCE Vim coactivam Intrinseca coercivity Maximus Working≤
BR (kg) BR (T) HCB
(Koe) 		HCB
(Ka / M) 		HCJ
(Koe) 		HCJ
(Ka / M) 		(BH) Carolus (mgoe) (BH) max
(KJ / M) 		℃
Max Min Max Min
N35 ≥11.8 ≥1.18 ≥10.8 ≥860 ≥12 ≥960 37 33 295 263 N ≤80
N38 ≥12.3 ≥1.23 ≥10.8 ≥860 ≥12 ≥960 39 36 310 287
N40 ≥12.7 ≥1.27 ≥11.0 ≥876 ≥12 ≥960 41 38 327 302
N42 ≥13.0 ≥1.30 ≥11.0 ≥876 ≥12 ≥960 43 40 343 320
N45 ≥13.3 ≥1.33 ≥11.0 ≥876 ≥12 ≥960 46 42 366 335
N48 ≥13.7 ≥1.37 ≥10.5 ≥836 ≥12 ≥960 49 45 390 358
N50 ≥14.0 ≥1.440 ≥10.5 ≥836 ≥12 ≥960 51 47 406 374
N52 ≥14.2 ≥1.42 ≥10.5 ≥836 ≥12 ≥960 53 49 422 390
N54 ≥14.4 ≥1.44 ≥10.5 ≥836 ≥11 ≥876 55 51 438 406
N35m ≥11.8 ≥1.18 ≥10.8 ≥860 ≥14 ≥1114 37 33 295 263 M ≤100
N38m ≥12.3 ≥1.23 ≥11.0 ≥876 ≥14 ≥1114 39 36 310 287
N40m ≥12.7 ≥1.27 ≥11.5 ≥915 ≥14 ≥1114 41 38 327 302
N42m ≥13.0 ≥1.30 ≥11.8 ≥939 ≥14 ≥1114 43 40 343 320
N45m ≥13.3 ≥1.33 ≥12.0 ≥956 ≥14 ≥1114 46 42 366 335
N48m ≥13.7 ≥1.37 ≥12.2 ≥972 ≥14 ≥1114 49 45 390 358
N50m ≥14.0 ≥1.440 ≥12.5 ≥995 ≥14 ≥1114 51 47 406 374
N52m ≥14.2 ≥1.42 ≥12.5 ≥995 ≥14 ≥1114 53 49 422 390
N33h ≥11.4 ≥1.14 ≥10.6 ≥844 ≥17 ≥1350 35 31 279 247 H ≤120
N35h ≥11.8 ≥1.18 ≥10.8 ≥860 ≥17 ≥1350 37 33 295 263
N38h ≥12.3 ≥1.23 ≥11.0 ≥876 ≥17 ≥1350 39 36 310 287
N40 ≥12.7 ≥1.27 ≥11.5 ≥916 ≥17 ≥1350 41 38 327 302
N42h ≥13.0 ≥1.30 ≥11.8 ≥940 ≥17 ≥1350 43 40 343 320
N45H ≥13.3 ≥1.33 ≥12.0 ≥955 ≥17 ≥1350 46 42 366 335
N48h ≥13.6 ≥1.36 ≥12.2 ≥971 ≥17 ≥1350 49 45 390 358
N50h ≥14 ≥1.4 ≥12.5 ≥995 ≥17 ≥1350 51 47 406 374
N52h ≥14.3 ≥1.43 ≥12.5 ≥995 ≥17 ≥1350 53 49 422 390
N33sh ≥11.4 ≥1.14 ≥10.6 ≥844 ≥20 ≥1592 35 31 279 247 Pungo ≤150
N35sh ≥11.8 ≥1.18 ≥10.8 ≥860 ≥20 ≥1592 37 33 295 263
N38sh ≥12.3 ≥1.23 ≥11.0 ≥876 ≥20 ≥1592 39 36 310 287
N40sh ≥12.6 ≥1.26 ≥11.5 ≥916 ≥20 ≥1592 41 38 327 302
N42sh ≥12.9 ≥1.29 ≥11.8 ≥940 ≥20 ≥1592 43 40 343 320
N45sh ≥13.2 ≥1.32 ≥12.0 ≥955 ≥20 ≥1592 46 42 366 335
N48sh ≥13.6 ≥1.36 ≥12.2 ≥971 ≥20 ≥1592 49 45 390 358
N50sh ≥14 ≥1.4 ≥12.5 ≥995 ≥20 ≥1592 51 47 406 374
N33uh ≥11.4 ≥1.14 ≥10.6 ≥844 ≥25 ≥1990 35 31 279 247 Ium ≤180
N35uh ≥11.8 ≥1.18 ≥10.8 ≥860 ≥25 ≥1990 37 33 295 263
N38uh ≥12.3 ≥1.23 ≥11.0 ≥876 ≥25 ≥1990 39 36 310 287
N40UH ≥12.6 ≥1.26 ≥11.5 ≥916 ≥25 ≥1990 41 38 327 302
N42uh ≥12.9 ≥1.29 ≥11.8 ≥940 ≥25 ≥1990 43 40 343 320
N45uh ≥13.2 ≥1.32 ≥12.0 ≥955 ≥25 ≥1990 46 42 366 335
N48uh ≥13.6 ≥1.36 ≥12.2 ≥971 ≥25 ≥1990 49 45 390 358
N28eh ≥10.4 ≥1.04 ≥9.50 ≥756 ≥30 ≥2388 30 26 239 207 EH ≤200
N30eh ≥10.8 ≥1.08 ≥9.50 ≥756 ≥30 ≥2388 32 28 255 223
N33eh ≥11.4 ≥1.14 ≥10.6 ≥844 ≥30 ≥2388 35 31 279 247
N35eh ≥11.8 ≥1.18 ≥10.8 ≥860 ≥30 ≥2388 37 33 295 263
N38eh ≥12.3 ≥1.23 ≥11.0 ≥876 ≥30 ≥2388 39 36 310 287
N4th ≥12.6 ≥1.26 ≥11.5 ≥916 ≥30 ≥2388 41 38 327 302
N42eh ≥12.9 ≥1.29 ≥11.8 ≥940 ≥30 ≥2388 43 41 343 320
N45eh ≥13.2 ≥1.32 ≥12.0 ≥955 ≥30 ≥2388 46 42 366 335
N30th ≥10.8 ≥1.08 ≥9.50 ≥756 ≥35 ≥2786 32 28 255 223 Th, ≤220
N33th ≥11.4 ≥1.14 ≥10.6 ≥844 ≥35 ≥2786 35 31 279 247
N35th ≥11.8 ≥1.18 ≥11.0 ≥876 ≥35 ≥2786 37 33 295 263
N38th ≥12.2 ≥1.22 ≥11.0 ≥876 ≥33 ≥2627 39 36 310 287
Dicta: Maximum opus temperatus pendeat in figura, magnitudine, et coating de magnetis, summa working temperatus in mensa est test notitia ad vexillum sample.3
Dimensiones et tolerantia
Vexillum uber D.od Id L W H
<5mm ± 0.1mm ± 0.1mm ± 0.1mm ± 0.1mm ± 0.1mm
<10mm ± 0.1mm ± 0.1mm ± 0.1mm ± 0.1mm ± 0.1mm
<20mm ± 0.1mm ± 0.1mm ± 0.1mm ± 0.1mm ± 0.1mm
<50mm ± 0.1mm ± 0.1mm ± 0.1mm ± 0.1mm ± 0.1mm
<100mm ± 0.15MM ± 0.15MM ± 0.15MM ± 0.15MM ± 0.15MM
> 100mm ± 0.2mm ± 0.2mm ± 0.2mm ± 0.2mm ± 0.2M
Figura Tractus Dimensio
AXIBILITER Diametro
Obstructum W≤100; XXX 30
Cylindrus 20≤H≤60; 40≤d≤200
25≤H≤35; 10ΑEN 		20≤H≤80; 25≤φ≤60
25≤H≤30; 10ΑÐ
Circulus 20≤H 25≤H≤45; 50≤d≤150; 8≤ (D-D) / II 25≤H≤40; 20≤d≤60; 8≤ (D-D) / II
Tile (arcus) 35≤W≤50; 15≤T≤40; 30≤H≤45 35≤W≤100; 15≤T≤30; 24≤≤H≤100
35≤W≤100; 25≤T≤40; 30≤H≤80
Superficies coating & Corrosio resistentia
Nickel (Ni-Cu-NI) Zinc (ZN) Epoxy Aureo
Genus Colo PRAEVALITAS Operatus
Temperamentum 		Commodum & idoneam Salis RAMULUS resistentia
Nickel (Nicuni) argentum 20-30 um ≤200 High oxidatio resistentia, bonum Glossa, firmum perficientur, diu muneris vitae > LXXII hrs
Zinc (ZN) caeruleus 10-20 um ≤160 Idoneam humilitatem requisita superficiem species & oxidatio resistentia > XLVIII hrs
Epoxy niger 10-30 um ≤120 apta summus anti-corrosio stricte atmospheric > XCVI hrs
Aureo Aureo 5-30 um ≤200 apta ornamentum accessiones, donum etc. > XXIV Hrs
Magnetize Direction 3
Disc & cylindri-per crassitudine Disc & cylindri-per diameter Spheres- per diameter

Vectes ad plana superficiebus

Poles parte superficiebus

Block- per crassitudine Longitudo per block- Arc- per diamer

Poles in maius plana superficiebus

Poles minores plana superficiebus

Poles in extra & intus facies

Arc- per longitudinem Ring- per superficiebus Ring- per superficiebus

Poles in extra & intus facies

Planar Octupole Magnetization

Planar Quadrupole Magnetization